Abstract The mechanical properties and corrosion performance of the N10276 alloy welded joint were investigated with nano-hardness testing and electrochemical measurement. The results showed that solidification mode changes from equiaxed crystal to columnar crystal from the center of the weldment to the fusion zone. With the increase of immersion times, the diameter of capacitance arc and the impedance modulus increase, and the corrosion resistance of HAZ decreases. The strengthening effect of welded metal was more obvious than that of heat affected zone for the nickel-based welded joint and especially in coarse grained heat affected zone, the hardening resulted from overheating was not apparent. Nickel-based weld metal with high content of alloying elements were often segregated at interdendritic regions or precipitated in grain interior under nonequilibrium solidification, which differ from conventional low alloy steel welded joint.

Abstract Plant height (PH) is controlled by quantitative trait loci (QTLs) in rice. In the present study, a recombinant inbred line population developed by crossing two rice cultivars, Lemont and Yangdao4, was grown in eight environments for QTL analysis. Multiple interval mapping detected 53 PH-QTLs, 39 of which clustered at 12 chromosome regions/putative loci. An examination of the 12 putative loci identified 24 alleles that are simultaneously involved in controlling PH. Linear regression analyses suggested that these 24 alleles function additively across the 12 loci to control PH, and plants carrying more PH-increasing alleles at the 12 loci were taller than those carrying more PH-decreasing alleles. Multiple comparison tests indicated that the effect of a single allele at the 12 loci was small and that multiple alleles must be pyramided to attain a statistically significant effect. The closest markers to the 12 loci can be used directly in marker-assisted breeding to manipulate PH.

Metal oxides (manganese oxide, MnO, manganese dioxide, MnO2, copper oxide, CuO, zinc oxide, ZnO and nickel oxide, NiO) doped carbon aerogel (CA) were prepared and used as catalysts in heterogeneous oxidation of phenol from aqueous solution in a three-dimensional (3D) electrode reactor. Textural characterization of metal oxides doped CA showed that the metal oxide nanoparticles are dispersed separately throughout the carbon matrix. The experimental results showed that phenol was degraded mainly by hydroxyl (•OH) radicals. The presence of metal oxides accelerated •OH radical generation. The •OH radical quantity depends on the type of metal oxide. The n-type semiconductor was more active than p-type semiconductor for •OH radical generation. Furthermore, acceleration effect of •OH radical generation catalyzed by metal oxides doped CA was investigated and demonstrated.